dc.contributor.authorRattiyakorn Rianyoien_US
dc.contributor.authorRuamporn Potongen_US
dc.contributor.authorAthipong Ngamjarurojanaen_US
dc.contributor.authorArnon Chaipanichen_US
dc.description.abstract© 2017, Springer Science+Business Media, LLC. PVDF-modified 0–3 connectivity cement-based/lead-free 0.94(Bi0.5Na0.5)TiO3–0.06BaTiO3piezoelectric ceramic composites were fabricated using 0.94(Bi0.5Na0.5)TiO3–0.06BaTiO3(BNBT), Portland cement, and polyvinylidene fluoride (PVDF). The microstructure, acoustic impedance (Zc), dielectric properties, and influence of poling temperature and electrical poling field on the piezoelectric coefficient (d33) and the total period of the poling process of composites with 50 vol% BNBT and 1–10 vol% PVDF were investigated. The results indicated that Zc, the dielectric constant, and the dielectric loss of the composites decrease as the PVDF content increases. The d33of the composites was found to enhance more clearly when the content of PVDF is more than 2 vol%. The d33results of the composites showed an optimum increase of 45% when 5 vol% PVDF was used (under an electrical poling field of 1.5 kV/mm and a poling temperature of 80°C). Moreover, these composites with PVDF were found to exhibit enhanced poling behavior in that the PVDF was able to reduce the total period of the poling process. Interestingly, the piezoelectric voltage coefficient (g33) of the composite with 5 vol% PVDF content had the highest value of 33.59 mV·m/N. Therefore, it can be safely concluded that this new kind of PVDF-modified 0–3 connectivity cement-based/lead-free 0.94(Bi0.5Na0.5)TiO3–0.06BaTiO3piezoelectric ceramic composite has the potential to be used in concrete as a sensor for structural health monitoring applications.en_US
dc.subjectMaterials Scienceen_US
dc.titlePoling effects and piezoelectric properties of PVDF-modified 0–3 connectivity cement-based/lead-free 0.94(Bi<inf>0.5</inf>Na<inf>0.5</inf>)TiO<inf>3</inf>–0.06BaTiO<inf>3</inf>piezoelectric ceramic compositesen_US
article.title.sourcetitleJournal of Materials Scienceen_US
article.volume53en_US Mai Universityen_US University of Technology systemen_US
Appears in Collections:CMUL: Journal Articles

Files in This Item:
There are no files associated with this item.

Items in CMUIR are protected by copyright, with all rights reserved, unless otherwise indicated.