Title: Effect of particle sizes of BaTiO<inf>3</inf>(BT) seed on microstructure and electrical properties of (Ba<inf>0.85</inf>Ca<inf>0.15</inf>)(Zr<inf>0.1</inf>Ti<inf>0.9</inf>)O<inf>3</inf>
Authors: Manlika Kamnoy
Piewpan Parjansri
Uraiwan Intatha
Sukum Eitssayeam
Tawee Tunkasiri
Keywords: Engineering
Materials Science
Issue Date: 1-Jan-2016
Abstract: © 2016 Trans Tech Publications, Switzerland. This study was conducted to find out the effect of particle sizes of BaTiO3(BT) seed on the microstructure and electrical properties of (Ba0.85Ca0.15)(Zr0.1Ti0.9)O3(BCZT) ceramics. The BT seeds were prepared by the molten salt method. The XRD patterns indicated that the BT seed powder showed a single pure perovskite phase when using a low temperature of ∼750°C. The particle sizes of BT seeds increased from ∼372 to ∼426 nm with increasing heating temperatures from 750 to 850°C. After that, the different BT seeds were mixed with BaCO3, CaCo3, ZrO2and TiO3from the solid state reaction method. The mixed powder was calcined and sintered at 1200 °C for 2 h and 1450 °C for 4 h, respectively. The microstructure, phase formation and electrical properties were investigated. All ceramic samples showed a pure perovskite phase. The density and average grain size values of ceramics were in the range of 5.36-5.47 g/cm3 and 9.83-11.86 μm, respectively. The highest values of dielectric constant (ϵr), piezoelectric constant (d33) were 3393 and 452 pC/N, respectively which was obtained for the sample of BT-seed size 372 nm doped.
ISSN: 10139826
Appears in Collections:CMUL: Journal Articles

Files in This Item:
There are no files associated with this item.

Items in CMUIR are protected by copyright, with all rights reserved, unless otherwise indicated.