Please use this identifier to cite or link to this item:
Title: Structural and magnetic properties of SiO<inf>2</inf>-CaO-Na<inf>2</inf>O-P<inf>2</inf>O<inf>5</inf>containing BaO-Fe<inf>2</inf>O<inf>3</inf>glass-ceramics
Authors: W. Leenakul
P. Kantha
N. Pisitpipathsin
G. Rujijanagul
S. Eitssayeam
K. Pengpat
Keywords: Materials Science
Physics and Astronomy
Issue Date: 1-Jan-2013
Abstract: The incorporation method was employed to produce bioactive glass-ceramics from the BaFe12O19-SiO2-CaO-Na2O-P2O5glass system. The ferrimagnetic BaFe12O19was first prepared using a simple mixed oxide method, where the oxide precursors of 45S5 bioglass were initially mixed and then melted to form glass. The devitrification of Na3Ca6(PO4)5and Fe3O4was observed in all of the quenched glass samples. The glass samples were then subjected to a heat treatment schedule for further crystallization. It was found that the small traces of BaFe12O19phases started to crystallize in high BF content samples of 20 and 40 wt%. These samples also exhibited good magnetic properties comparable to that of other magnetic glass-ceramics. The bioactivity of the BF glass-ceramics improved with increasing BF content as was evident by the formation of bone-like apatite layers on the surface of all of the glass-ceramics after soaking in SBF for 14 days. The results support the use of these bioactive glass-ceramics for hyperthermia treatment within the human body. © 2012 Elsevier B.V. All rights reserved.
ISSN: 03048853
Appears in Collections:CMUL: Journal Articles

Files in This Item:
There are no files associated with this item.

Items in CMUIR are protected by copyright, with all rights reserved, unless otherwise indicated.